Compare Materials

Properties

67
50
Bulk Modulus (GPa)
2.71
1.77
Density (g/cm3)
69
45
Elastic (Young's) Modulus (GPa)
45
18.5
Electrical Conductivity (% IACS)
5
15
Elongation at Break: Typical (%)
638
605
Maximum Temperature: Onset of Melting (Solidus) (°C)
0.33
0.35
Poisson's Ratio
25
17
Shear Modulus (GPa)
150
150
Speed of Sound (103 m/s)
24
28
Stiffness-to-Weight Ratio: Bulk (MN-m/kg)
9.2
9.6
Stiffness-to-Weight Ratio: Shear (MN-m/kg)
25
25
Stiffness-to-Weight Ratio: Tensile (MN-m/kg)
62
160
Strength-to-Weight Ratio: Tensile, Ultimate (kN-m/kg)
55
120
Strength-to-Weight Ratio: Tensile, Yield (kN-m/kg)
170
290
Tensile Strength: Ultimate (MPa)
150
220
Tensile Strength: Yield (Proof) (MPa)
173
96
Thermal Conductivity: Ambient (W/m-K)
23.6
26
Thermal Expansion: 20 to 100°C (µm/m-K)

4 mutual properties could not be displayed because they require login.

'