Compare Materials

Properties

98
110
Bulk Modulus (GPa)
4.5
4.4
Density (g/cm3)
100
115
Elastic (Young's) Modulus (GPa)
37
10
Electrical Conductivity (% IACS)
20 to 30
8 to 15
Elongation at Break: Typical (%)
0.33
0.33
Poisson's Ratio
39
42
Shear Modulus (GPa)
140
160
Speed of Sound (103 m/s)
21
25
Stiffness-to-Weight Ratio: Bulk (MN-m/kg)
8.6
9.5
Stiffness-to-Weight Ratio: Shear (MN-m/kg)
22
26
Stiffness-to-Weight Ratio: Tensile (MN-m/kg)
73 to 140
220 to 260
Strength-to-Weight Ratio: Tensile, Ultimate (kN-m/kg)
53 to 130
200 to 250
Strength-to-Weight Ratio: Tensile, Yield (kN-m/kg)
330 to 660
990 to 1170
Tensile Strength: Ultimate (MPa)
240 to 590
890 to 1100
Tensile Strength: Yield (Proof) (MPa)
16
7
Thermal Conductivity: Ambient (W/m-K)
9
8.5
Thermal Expansion: 20 to 100°C (µm/m-K)

7 mutual properties could not be displayed because they require login.

'