Compare Materials

Properties

3.1
3.5 to 4.8
Bulk Modulus (GPa)
1.2
1.04 to 1.05
Density (g/cm3)
15
18 to 20
Dielectric Strength (Breakdown Potential) (MV/m)
2.3
1.9 to 2.9
Elastic (Young's) Modulus (GPa)
110
2 to 40
Elongation at Break: Typical (%)
93
62 to 76
Flexural Strength (MOR): Typical (MPa)
150
100
Glass Transition Temperature (°C)
26
18
Limiting Oxygen Index (LOI) (%)
120
70
Maximum Temperature: Typical Guideline (°C)
0.38
0.4 to 0.41
Poisson's Ratio
0.8
0.95 to 1.4
Shear Modulus (GPa)
1200
1250 to 1400
Specific Heat Capacity: Conventional (J/kg-K)
1400
1300 to 1400
Specific Heat Capacity: Volumetric (103 J/m3-K)
43
42 to 52
Speed of Sound (103 m/s)
2.6
3.3 to 4.6
Stiffness-to-Weight Ratio: Bulk (MN-m/kg)
0.66
0.91 to 1.3
Stiffness-to-Weight Ratio: Shear (MN-m/kg)
1.9
1.8 to 2.7
Stiffness-to-Weight Ratio: Tensile (MN-m/kg)
77
59 to 72
Strength-to-Weight Ratio: Flexural (kN-m/kg)
54
30 to 43
Strength-to-Weight Ratio: Tensile, Ultimate (kN-m/kg)
65
32 to 46
Tensile Strength: Ultimate (MPa)
0.2
0.14 to 0.22
Thermal Conductivity: Ambient (W/m-K)
150
100 to 105
Vicat Softening Temperature (°C)
0.15
0.04 to 0.08
Water Absorption: After 24 Hours (%)

4 mutual properties could not be displayed because they require login.

'