3003 Aluminum vs. UF
3003 aluminum and UF belong to fundamentally different material chemistries. 3003 aluminum is a metal, while UF is a polymeric material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 13 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is 3003 aluminum and the bottom bar is UF.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 9.0 |
| Elongation at Break, % | 1.1 to 28 | |
| 1.0 |
| Tensile Strength: Ultimate (UTS), MPa | 110 to 240 | |
| 30 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 900 | |
| 1200 |
| Thermal Conductivity, W/m-K | 180 | |
| 0.4 |
| Thermal Expansion, µm/m-K | 23 | |
| 55 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.8 | |
| 1.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 3.3 |
| Stiffness to Weight: Bending, points | 50 | |
| 46 |
| Strength to Weight: Axial, points | 11 to 24 | |
| 5.6 |
| Strength to Weight: Bending, points | 18 to 30 | |
| 14 |
| Thermal Diffusivity, mm2/s | 71 | |
| 0.22 |
| Thermal Shock Resistance, points | 4.7 to 10 | |
| 4.3 |