6151 Aluminum vs. C72150 Copper-nickel
6151 aluminum belongs to the aluminum alloys classification, while C72150 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6151 aluminum and the bottom bar is C72150 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 150 |
| Elongation at Break, % | 1.1 to 5.7 | |
| 29 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 55 |
| Shear Strength, MPa | 190 to 200 | |
| 320 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 340 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 270 to 280 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 600 |
| Melting Completion (Liquidus), °C | 650 | |
| 1210 |
| Melting Onset (Solidus), °C | 590 | |
| 1250 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 410 |
| Thermal Conductivity, W/m-K | 170 | |
| 22 |
| Thermal Expansion, µm/m-K | 23 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 3.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 3.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 45 |
| Density, g/cm3 | 2.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 6.1 |
| Embodied Energy, MJ/kg | 150 | |
| 88 |
| Embodied Water, L/kg | 1180 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.5 to 18 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 520 to 580 | |
| 150 |
| Stiffness to Weight: Axial, points | 14 | |
| 9.1 |
| Stiffness to Weight: Bending, points | 50 | |
| 20 |
| Strength to Weight: Axial, points | 34 | |
| 15 |
| Strength to Weight: Bending, points | 39 | |
| 15 |
| Thermal Diffusivity, mm2/s | 70 | |
| 6.0 |
| Thermal Shock Resistance, points | 15 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 95.6 to 98.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 52.5 to 57 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.45 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 | |
| 43 to 46 |
| Silicon (Si), % | 0.6 to 1.2 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.5 |