7010 Aluminum vs. 520.0 Aluminum
Both 7010 aluminum and 520.0 aluminum are aluminum alloys. They have a moderately high 92% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 7010 aluminum and the bottom bar is 520.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 66 |
| Elongation at Break, % | 3.9 to 6.8 | |
| 14 |
| Fatigue Strength, MPa | 160 to 190 | |
| 55 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 25 |
| Shear Strength, MPa | 300 to 340 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 590 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 410 to 540 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Melting Completion (Liquidus), °C | 630 | |
| 600 |
| Melting Onset (Solidus), °C | 480 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 910 |
| Thermal Conductivity, W/m-K | 150 | |
| 87 |
| Thermal Expansion, µm/m-K | 24 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 21 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 72 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 9.8 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1120 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 to 33 | |
| 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1230 to 2130 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 52 |
| Strength to Weight: Axial, points | 47 to 54 | |
| 35 |
| Strength to Weight: Bending, points | 47 to 52 | |
| 41 |
| Thermal Diffusivity, mm2/s | 58 | |
| 37 |
| Thermal Shock Resistance, points | 22 to 26 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 87.9 to 90.6 | |
| 87.9 to 90.5 |
| Chromium (Cr), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 1.5 to 2.0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 2.1 to 2.6 | |
| 9.5 to 10.6 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.15 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.12 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.060 | |
| 0 to 0.25 |
| Zinc (Zn), % | 5.7 to 6.7 | |
| 0 to 0.15 |
| Zirconium (Zr), % | 0.1 to 0.16 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |