7075 Aluminum vs. FEP
7075 aluminum and FEP belong to fundamentally different material chemistries. 7075 aluminum is a metal, while FEP is a polymeric material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (31, in this case) are not shown.
For each property being compared, the top bar is 7075 aluminum and the bottom bar is FEP.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 0.43 |
| Elongation at Break, % | 1.8 to 12 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 590 | |
| 20 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Onset (Solidus), °C | 480 | |
| 260 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 1170 |
| Thermal Conductivity, W/m-K | 130 | |
| 0.22 |
| Thermal Expansion, µm/m-K | 23 | |
| 95 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.0 | |
| 2.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 0.11 |
| Stiffness to Weight: Bending, points | 46 | |
| 12 |
| Strength to Weight: Axial, points | 22 to 54 | |
| 2.6 |
| Strength to Weight: Bending, points | 28 to 52 | |
| 7.6 |
| Thermal Diffusivity, mm2/s | 50 | |
| 0.088 |
| Thermal Shock Resistance, points | 10 to 25 | |
| 35 |