AISI 431 Stainless Steel vs. SAE-AISI 1132 Steel

Both AISI 431 stainless steel and SAE-AISI 1132 steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 431 stainless steel and the bottom bar is SAE-AISI 1132 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
190 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 15 to 17
14 to 18
Fatigue Strength, MPa 430 to 610
240 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 550 to 840
400 to 440
Tensile Strength: Ultimate (UTS), MPa 890 to 1380
640 to 720
Tensile Strength: Yield (Proof), MPa 710 to 1040
350 to 590

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 850
400
Melting Completion (Liquidus), °C 1510
1460
Melting Onset (Solidus), °C 1450
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 26
51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.4
Embodied Energy, MJ/kg 31
19
Embodied Water, L/kg 120
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 180
93 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 1270 to 2770
330 to 940
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32 to 50
23 to 25
Strength to Weight: Bending, points 27 to 36
21 to 23
Thermal Diffusivity, mm2/s 7.0
14
Thermal Shock Resistance, points 28 to 43
19 to 22

Alloy Composition

Carbon (C), % 0 to 0.2
0.24 to 0.34
Chromium (Cr), % 15 to 17
0
Iron (Fe), % 78.2 to 83.8
97.8 to 98.3
Manganese (Mn), % 0 to 1.0
1.4 to 1.7
Nickel (Ni), % 1.3 to 2.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0.080 to 0.13