Remarks

Both ABS and PBT are thermoplastics.

There are 9 material properties with values for both materials. Properties with values for just one material (7 in this case) are not shown.

Properties in Common

Density
1.0 to 1.4 g/cm3
1.3 to 1.5 g/cm3
Elastic Modulus
2.0 to 2.6 GPa
2.7 to 8.7 GPa
Elongation
3.5 to 50 %
2.5 to 43 %
Flexural Modulus
2.1 to 7.6 GPa
2.6 to 9.1 GPa
Flexural Strength
72 to 97 MPa
79 to 210 MPa
Heat Deflection At 1.82 MPa
76 to 110 °C
4.0 °C
Heat Deflection At 455 KPa
83 to 110 °C
160 °C
Strength-to-weight
37 to 79 kN-m/kg
45 to 93 kN-m/kg
UTS
37 to 110 MPa
58 to 140 MPa

The length of each bar compares the given value to the highest value in the database.

Properties Not in Common

Dielectric Constant: 3.1 to 3.2 (ABS)

Dielectric Strength: 15 to 16 kV/mm (ABS)

Glass Transition: 40 °C (PBT)

Oxygen Index: 20 % (PBT)

Melting Onset: 230 °C (PBT)

Specific Heat: 1040 to 1200 J/kg-K (PBT)

Thermal Expansion: 81 to 95 µm/m-K (ABS)