Alumina vs. 5086 Aluminum
Alumina and 5086 aluminum belong to fundamentally different material chemistries. Alumina is a ceramic material, while 5086 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (29, in this case) are not shown.
For each property being compared, the top bar is alumina and the bottom bar is 5086 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 to 370 | |
68 |
Poisson's Ratio | 0.22 to 0.24 | |
0.33 |
Tensile Strength: Ultimate (UTS), MPa | 210 to 290 | |
270 to 390 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 650 to 1730 | |
190 |
Melting Onset (Solidus), °C | 2040 | |
590 |
Specific Heat Capacity, J/kg-K | 870 to 940 | |
900 |
Thermal Conductivity, W/m-K | 14 to 30 | |
130 |
Thermal Expansion, µm/m-K | 6.7 to 8.2 | |
24 |
Otherwise Unclassified Properties
Density, g/cm3 | 3.4 to 4.1 | |
2.7 |
Common Calculations
Stiffness to Weight: Axial, points | 35 to 53 | |
14 |
Stiffness to Weight: Bending, points | 57 to 62 | |
50 |
Strength to Weight: Axial, points | 14 to 23 | |
28 to 40 |
Strength to Weight: Bending, points | 19 to 28 | |
34 to 44 |
Thermal Diffusivity, mm2/s | 3.7 to 10 | |
52 |
Thermal Shock Resistance, points | 4.9 to 14 | |
12 to 17 |