Alumina vs. EN 1.7321 Steel
Alumina and EN 1.7321 steel belong to fundamentally different material chemistries. Alumina is a ceramic material, while EN 1.7321 steel is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is alumina and the bottom bar is EN 1.7321 steel.
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 to 370 | |
190 |
Poisson's Ratio | 0.22 to 0.24 | |
0.29 |
Tensile Strength: Ultimate (UTS), MPa | 210 to 290 | |
490 to 1460 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 650 to 1730 | |
410 |
Melting Onset (Solidus), °C | 2040 | |
1420 |
Specific Heat Capacity, J/kg-K | 870 to 940 | |
470 |
Thermal Conductivity, W/m-K | 14 to 30 | |
45 |
Thermal Expansion, µm/m-K | 6.7 to 8.2 | |
13 |
Otherwise Unclassified Properties
Density, g/cm3 | 3.4 to 4.1 | |
7.9 |
Common Calculations
Stiffness to Weight: Axial, points | 35 to 53 | |
13 |
Stiffness to Weight: Bending, points | 57 to 62 | |
24 |
Strength to Weight: Axial, points | 14 to 23 | |
17 to 52 |
Strength to Weight: Bending, points | 19 to 28 | |
18 to 36 |
Thermal Diffusivity, mm2/s | 3.7 to 10 | |
12 |
Thermal Shock Resistance, points | 4.9 to 14 | |
14 to 43 |