Alumina vs. PCTFE
Alumina and PCTFE belong to fundamentally different material chemistries. Alumina is a ceramic material, while PCTFE is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 18 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is alumina and the bottom bar is PCTFE.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 1920 to 2750 | |
| 38 |
| Elastic (Young's, Tensile) Modulus, GPa | 220 to 370 | |
| 1.4 |
| Flexural Strength, MPa | 260 to 430 | |
| 59 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 290 | |
| 36 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 650 to 1730 | |
| 150 |
| Melting Onset (Solidus), °C | 2040 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 870 to 940 | |
| 920 |
| Thermal Conductivity, W/m-K | 14 to 30 | |
| 0.21 |
| Thermal Expansion, µm/m-K | 6.7 to 8.2 | |
| 130 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 8.9 to 12 | |
| 21 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 6.2 to 14 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.4 to 4.1 | |
| 2.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 35 to 53 | |
| 0.37 |
| Stiffness to Weight: Bending, points | 57 to 62 | |
| 17 |
| Strength to Weight: Axial, points | 14 to 23 | |
| 4.6 |
| Strength to Weight: Bending, points | 19 to 28 | |
| 11 |
| Thermal Diffusivity, mm2/s | 3.7 to 10 | |
| 0.11 |
| Thermal Shock Resistance, points | 4.9 to 14 | |
| 14 |