Annealed AISI 304 vs. Annealed AISI 410
Both annealed AISI 304 and annealed AISI 410 are iron alloys. Both are furnished in the annealed condition. They have 84% of their average alloy composition in common.
For each property being compared, the top bar is annealed AISI 304 and the bottom bar is annealed AISI 410.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 43 | |
| 22 |
| Fatigue Strength, MPa | 210 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Reduction in Area, % | 53 | |
| 47 |
| Rockwell B Hardness | 79 | |
| 84 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Shear Strength, MPa | 400 | |
| 330 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 520 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 420 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 710 | |
| 710 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1530 |
| Melting Onset (Solidus), °C | 1400 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 30 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 7.0 |
| Calomel Potential, mV | -80 | |
| -150 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 1.9 |
| Embodied Energy, MJ/kg | 43 | |
| 27 |
| Embodied Water, L/kg | 150 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 97 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 210 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 19 |
| Strength to Weight: Bending, points | 20 | |
| 19 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 8.1 |
| Thermal Shock Resistance, points | 12 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 18 to 20 | |
| 11.5 to 13.5 |
| Iron (Fe), % | 66.5 to 74 | |
| 83.5 to 88.4 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 8.0 to 10.5 | |
| 0 to 0.75 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |