Borosilicate Glass vs. C63000 Bronze
Borosilicate glass and C63000 bronze belong to fundamentally different material chemistries. Borosilicate glass is a ceramic material, while C63000 bronze is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is borosilicate glass and the bottom bar is C63000 bronze.
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 67 to 80 | |
120 |
Poisson's Ratio | 0.21 | |
0.34 |
Tensile Strength: Ultimate (UTS), MPa | 280 | |
660 to 790 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 360 | |
230 |
Melting Onset (Solidus), °C | 560 | |
1040 |
Specific Heat Capacity, J/kg-K | 830 | |
440 |
Thermal Conductivity, W/m-K | 1.2 | |
39 |
Thermal Expansion, µm/m-K | 3.3 to 5.1 | |
18 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.2 to 2.6 | |
8.2 |
Common Calculations
Stiffness to Weight: Axial, points | 15 to 17 | |
7.9 |
Stiffness to Weight: Bending, points | 55 to 61 | |
20 |
Strength to Weight: Axial, points | 30 to 35 | |
22 to 26 |
Strength to Weight: Bending, points | 36 to 43 | |
20 to 23 |
Thermal Diffusivity, mm2/s | 0.54 to 0.63 | |
11 |
Thermal Shock Resistance, points | 50 to 91 | |
23 to 27 |