Borosilicate Glass vs. C79200 Nickel Silver

Borosilicate glass and C79200 nickel silver belong to fundamentally different material chemistries. Borosilicate glass is a ceramic material, while C79200 nickel silver is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is borosilicate glass and the bottom bar is C79200 nickel silver.

Borosilicate GlassUNS C79200 (CW404J) Leaded Nickel Silver
Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 67 to 80
120
Poisson's Ratio 0.21
0.32
Tensile Strength: Ultimate (UTS), MPa 280
480 to 540

Thermal Properties

Maximum Temperature: Mechanical, °C 360
170
Melting Onset (Solidus), °C 560
910
Specific Heat Capacity, J/kg-K 830
390
Thermal Conductivity, W/m-K 1.2
42
Thermal Expansion, µm/m-K 3.3 to 5.1
19

Otherwise Unclassified Properties

Density, g/cm3 2.2 to 2.6
8.4

Common Calculations

Stiffness to Weight: Axial, points 15 to 17
7.7
Stiffness to Weight: Bending, points 55 to 61
19
Strength to Weight: Axial, points 30 to 35
16 to 18
Strength to Weight: Bending, points 36 to 43
16 to 18
Thermal Diffusivity, mm2/s 0.54 to 0.63
13
Thermal Shock Resistance, points 50 to 91
16 to 18