Carbon-carbon vs. CPVC
Carbon-carbon and CPVC belong to fundamentally different material chemistries. Carbon-carbon is a ceramic material, while CPVC is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is carbon-carbon and the bottom bar is CPVC.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 240 | |
| 70 |
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 2.8 |
| Tensile Strength: Ultimate (UTS), MPa | 19 | |
| 50 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 2400 | |
| 80 |
| Specific Heat Capacity, J/kg-K | 760 | |
| 780 |
| Thermal Conductivity, W/m-K | 40 | |
| 0.31 |
| Thermal Expansion, µm/m-K | 4.0 | |
| 65 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | -5.0 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 1.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 31 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 89 | |
| 32 |
| Strength to Weight: Axial, points | 3.0 | |
| 9.4 |
| Strength to Weight: Bending, points | 9.1 | |
| 20 |
| Thermal Diffusivity, mm2/s | 31 | |
| 0.27 |
| Thermal Shock Resistance, points | 3.5 | |
| 20 |