Carbon-carbon vs. DAP
Carbon-carbon and DAP belong to fundamentally different material chemistries. Carbon-carbon is a ceramic material, while DAP is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 14 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is carbon-carbon and the bottom bar is DAP.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 240 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 13 |
| Tensile Strength: Ultimate (UTS), MPa | 19 | |
| 28 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 760 | |
| 1450 |
| Thermal Conductivity, W/m-K | 40 | |
| 0.6 |
| Thermal Expansion, µm/m-K | 4.0 | |
| 25 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | -5.0 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 1.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 31 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 89 | |
| 46 |
| Strength to Weight: Axial, points | 3.0 | |
| 4.5 |
| Strength to Weight: Bending, points | 9.1 | |
| 12 |
| Thermal Diffusivity, mm2/s | 31 | |
| 0.24 |
| Thermal Shock Resistance, points | 3.5 | |
| 6.3 |