Carbon-carbon vs. PVF
Carbon-carbon and PVF belong to fundamentally different material chemistries. Carbon-carbon is a ceramic material, while PVF is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 9 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is carbon-carbon and the bottom bar is PVF.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.7 | |
| 1.4 |
| Maximum Temperature: Mechanical, °C | 2400 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 760 | |
| 1300 |
| Strength to Weight: Axial, points | 3.0 | |
| 13 |
| Strength to Weight: Bending, points | 9.1 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 19 | |
| 65 |
| Thermal Conductivity, W/m-K | 40 | |
| 0.13 |
| Thermal Diffusivity, mm2/s | 31 | |
| 0.071 |
| Thermal Expansion, µm/m-K | 4.0 | |
| 100 |