CA vs. Glass-bonded Mica
CA and glass-bonded mica belong to fundamentally different material chemistries. CA is a polymeric material, while glass-bonded mica is ceramic. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 12 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is CA and the bottom bar is glass-bonded mica.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Strength, MPa | 40 to 55 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 30 to 37 | |
| 39 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 1500 | |
| 500 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 23 |
| Thermal Expansion, µm/m-K | 14 | |
| 6.7 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.6 | |
| 6.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 15 | |
| 20 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 16 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 2.6 |
Common Calculations
| Strength to Weight: Axial, points | 6.4 to 7.9 | |
| 4.1 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 9.7 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 18 |