EN 1.4315 Stainless Steel vs. EN 1.1192 Steel

Both EN 1.4315 stainless steel and EN 1.1192 steel are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4315 stainless steel and the bottom bar is EN 1.1192 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 630
520 to 1810

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 960
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
19
Embodied Water, L/kg 150
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
18 to 64
Strength to Weight: Bending, points 21
18 to 42
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 14
16 to 58

Alloy Composition

Carbon (C), % 0 to 0.060
0.42 to 0.5
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 65.7 to 73.9
98.1 to 99.08
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Nickel (Ni), % 8.0 to 11
0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025