ECTFE vs. ABS
Both ECTFE and ABS are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ECTFE and the bottom bar is ABS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 | |
| 2.0 to 2.6 |
| Elongation at Break, % | 230 | |
| 3.5 to 50 |
| Flexural Modulus, GPa | 1.7 | |
| 2.1 to 7.6 |
| Flexural Strength, MPa | 47 | |
| 72 to 97 |
| Rockwell R Hardness | 93 | |
| 100 to 110 |
| Tensile Strength: Ultimate (UTS), MPa | 49 | |
| 37 to 110 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 91 | |
| 76 to 110 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 110 | |
| 83 to 110 |
| Thermal Expansion, µm/m-K | 100 | |
| 81 to 95 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.3 | |
| 3.1 to 3.2 |
| Dielectric Strength (Breakdown Potential), kV/mm | 18 | |
| 15 to 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 1.0 to 1.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.52 | |
| 0.79 to 1.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 30 to 44 |
| Strength to Weight: Axial, points | 8.1 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 18 | |
| 24 to 37 |
| Thermal Shock Resistance, points | 22 | |
| 11 to 50 |