Grade 200 Maraging Steel vs. ASTM A209 Steel

Both grade 200 maraging steel and ASTM A209 steel are iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 200 maraging steel and the bottom bar is ASTM A209 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 9.1 to 18
34
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 600 to 890
280 to 310
Tensile Strength: Ultimate (UTS), MPa 970 to 1500
420 to 460
Tensile Strength: Yield (Proof), MPa 690 to 1490
220 to 250

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420 to 1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.4
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 4.5
1.5
Embodied Energy, MJ/kg 59
20
Embodied Water, L/kg 140
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 160
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 1240 to 5740
130 to 170
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 33 to 51
15 to 16
Strength to Weight: Bending, points 27 to 35
16 to 17
Thermal Shock Resistance, points 29 to 45
12 to 14