Grade 200 Maraging Steel vs. ASTM A732 Cast Steel
Both grade 200 maraging steel and ASTM A732 cast steel are iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 200 maraging steel and the bottom bar is ASTM A732 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 9.1 to 18 | |
| 4.0 to 25 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 72 to 73 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1500 | |
| 460 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 690 to 1490 | |
| 310 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 to 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 to 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 to 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 to 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 2.0 to 3.8 |
| Density, g/cm3 | 8.2 | |
| 7.8 to 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 1.4 to 1.7 |
| Embodied Energy, MJ/kg | 59 | |
| 19 to 24 |
| Embodied Water, L/kg | 140 | |
| 47 to 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 45 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1240 to 5740 | |
| 260 to 4770 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 33 to 51 | |
| 16 to 52 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 17 to 37 |
| Thermal Shock Resistance, points | 29 to 45 | |
| 14 to 43 |