Grade 350 Maraging Steel vs. C53400 Bronze
Grade 350 maraging steel belongs to the iron alloys classification, while C53400 bronze belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 350 maraging steel and the bottom bar is C53400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 2420 | |
| 330 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 200 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1050 |
| Melting Onset (Solidus), °C | 1420 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 32 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 3.0 |
| Embodied Energy, MJ/kg | 74 | |
| 49 |
| Embodied Water, L/kg | 160 | |
| 350 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 38 to 82 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 29 to 49 | |
| 12 to 20 |
| Thermal Shock Resistance, points | 35 to 74 | |
| 12 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 11.5 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 91.8 to 95.7 |
| Iron (Fe), % | 61.2 to 64.6 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 18 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0.030 to 0.35 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 3.5 to 5.8 |
| Titanium (Ti), % | 1.3 to 1.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.3 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |