H02 C70600 Copper-nickel vs. H02 C76200 Nickel Silver
Both H02 C70600 copper-nickel and H02 C76200 nickel silver are copper alloys. Both are furnished in the H02 (half hard) temper. They have 70% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is H02 C70600 copper-nickel and the bottom bar is H02 C76200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 74 | |
| 85 |
| Rockwell Superficial 30T Hardness | 67 | |
| 73 |
| Shear Modulus, GPa | 46 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 170 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1030 |
| Melting Onset (Solidus), °C | 1100 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 44 | |
| 45 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.8 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.9 | |
| 9.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 29 |
| Density, g/cm3 | 8.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.6 |
| Embodied Energy, MJ/kg | 51 | |
| 57 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 14 | |
| 19 |
| Strength to Weight: Bending, points | 15 | |
| 19 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 15 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 84.7 to 90 | |
| 57 to 61 |
| Iron (Fe), % | 1.0 to 1.8 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 9.0 to 11 | |
| 11 to 13.5 |
| Zinc (Zn), % | 0 to 1.0 | |
| 24.2 to 32 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |