HDPE vs. PA 6/10
Both HDPE and PA 6/10 are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is HDPE and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 to 1.3 | |
| 1.1 |
| Elongation at Break, % | 2.5 to 100 | |
| 110 to 120 |
| Flexural Modulus, GPa | 4.0 to 7.5 | |
| 1.4 to 2.0 |
| Impact Strength: Notched Izod, J/m | 50 to 260 | |
| 85 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 80 |
| Specific Heat Capacity, J/kg-K | 1330 to 2400 | |
| 1510 |
| Strength to Weight: Axial, points | 6.9 to 17 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 19 to 32 | |
| 25 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 24 to 80 | |
| 45 to 60 |