LCP vs. POM-H
Both LCP and POM-H are thermoplastics. There are 7 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is POM-H.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 7.0 to 55 |
| Flexural Modulus, GPa | 9.0 to 23 | |
| 2.9 to 4.3 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1250 to 1460 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 11 to 13 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 22 to 26 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 60 to 67 |