LCP vs. Ionomer
Both LCP and ionomer are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is ionomer.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.94 |
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 0.4 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 350 |
| Melting Onset (Solidus), °C | 280 | |
| 94 |
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 0.24 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 26 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 11 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 37 |