LCP vs. LDPE
Both LCP and LDPE are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is LDPE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.92 |
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 0.3 |
| Maximum Temperature: Decomposition, °C | 520 | |
| 400 |
| Melting Onset (Solidus), °C | 280 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 2300 |
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 0.18 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 24 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 2.1 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 8.8 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 7.0 |