LCP vs. PVC-P
Both LCP and PVC-P are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is PVC-P.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 1.4 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 180 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 16 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 520 | |
| 250 |
| Melting Onset (Solidus), °C | 280 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1400 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.4 |
| Limiting Oxygen Index (LOI), % | 35 | |
| 44 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 0.57 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 28 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 3.2 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 10 |