LCP vs. PA 11
Both LCP and PA 11 are thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is PA 11.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 0.4 to 1.3 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 80 to 130 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 25 to 51 |
Thermal Properties
| Melting Onset (Solidus), °C | 280 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1740 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.0 |
| Limiting Oxygen Index (LOI), % | 35 | |
| 29 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 0.22 to 0.71 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 24 to 36 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 6.7 to 14 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 18 to 30 |