LCP vs. PP Homopolymer
Both LCP and PP homopolymer are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is PP homopolymer.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.91 to 1.2 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 3.0 to 80 |
| Flexural Modulus, GPa | 9.0 to 23 | |
| 1.5 to 7.0 |
| Flexural Strength, MPa | 160 to 320 | |
| 41 to 100 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 240 to 270 | |
| 73 to 160 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1230 to 1900 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 27 to 37 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 36 to 93 |