LCP vs. Sandstone
LCP and sandstone belong to fundamentally different material chemistries. LCP is a polymeric material, while sandstone is ceramic. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 8 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is sandstone.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 2.6 |
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 38 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 880 |
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 43 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 0.43 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 2.1 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 4.0 |