LCP vs. UHMW-PE
Both LCP and UHMW-PE are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is UHMW-PE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.94 |
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 0.8 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 400 |
| Melting Onset (Solidus), °C | 280 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1750 |
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 0.47 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 33 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 14 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 49 |