MDF vs. R30035 Cobalt
MDF and R30035 cobalt belong to fundamentally different material chemistries. MDF is a polymeric material, while R30035 cobalt is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is MDF and the bottom bar is R30035 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 | |
| 220 to 230 |
| Elongation at Break, % | 0.5 | |
| 9.0 to 46 |
| Poisson's Ratio | 0.25 | |
| 0.29 |
| Shear Modulus, GPa | 2.5 | |
| 84 to 89 |
| Tensile Strength: Ultimate (UTS), MPa | 18 | |
| 900 to 1900 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 1700 | |
| 440 |
| Thermal Conductivity, W/m-K | 0.3 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.75 | |
| 8.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.0 | |
| 14 to 15 |
| Stiffness to Weight: Bending, points | 71 | |
| 23 to 24 |
| Strength to Weight: Axial, points | 6.7 | |
| 29 to 61 |
| Strength to Weight: Bending, points | 20 | |
| 24 to 39 |
| Thermal Diffusivity, mm2/s | 0.24 | |
| 3.0 |
| Thermal Shock Resistance, points | 27 | |
| 23 to 46 |