PVC-P vs. Mullite
PVC-P and mullite belong to fundamentally different material chemistries. PVC-P is a polymeric material, while mullite is ceramic. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PVC-P and the bottom bar is mullite.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.4 | |
| 110 to 170 |
| Poisson's Ratio | 0.39 | |
| 0.25 |
| Tensile Strength: Ultimate (UTS), MPa | 16 | |
| 160 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 75 | |
| 1680 |
| Specific Heat Capacity, J/kg-K | 1400 | |
| 950 |
| Thermal Conductivity, W/m-K | 0.17 | |
| 3.5 to 11 |
| Thermal Expansion, µm/m-K | 160 | |
| 5.8 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 5.8 | |
| 8.0 |
| Dielectric Strength (Breakdown Potential), kV/mm | 20 | |
| 16 to 17 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 11 | |
| 10 to 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 2.7 to 3.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.57 | |
| 22 to 31 |
| Stiffness to Weight: Bending, points | 28 | |
| 58 to 62 |
| Strength to Weight: Axial, points | 3.2 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 10 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 0.090 | |
| 1.4 to 3.7 |
| Thermal Shock Resistance, points | 4.9 | |
| 12 to 19 |