PVC-P vs. SAE-AISI 1552 Steel
PVC-P and SAE-AISI 1552 steel belong to fundamentally different material chemistries. PVC-P is a polymeric material, while SAE-AISI 1552 steel is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 16 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is PVC-P and the bottom bar is SAE-AISI 1552 steel.
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 1.4 | |
190 |
Elongation at Break, % | 180 | |
11 to 14 |
Poisson's Ratio | 0.39 | |
0.29 |
Tensile Strength: Ultimate (UTS), MPa | 16 | |
760 to 840 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 75 | |
400 |
Melting Onset (Solidus), °C | 190 | |
1420 |
Specific Heat Capacity, J/kg-K | 1400 | |
470 |
Thermal Conductivity, W/m-K | 0.17 | |
51 |
Thermal Expansion, µm/m-K | 160 | |
11 |
Otherwise Unclassified Properties
Density, g/cm3 | 1.4 | |
7.8 |
Common Calculations
Stiffness to Weight: Axial, points | 0.57 | |
13 |
Stiffness to Weight: Bending, points | 28 | |
24 |
Strength to Weight: Axial, points | 3.2 | |
27 to 30 |
Strength to Weight: Bending, points | 10 | |
24 to 25 |
Thermal Diffusivity, mm2/s | 0.090 | |
14 |
Thermal Shock Resistance, points | 4.9 | |
26 to 29 |