PA 4/6 vs. 50Cr-50Ni-Cb Alloy
PA 4/6 and 50Cr-50Ni-Cb alloy belong to fundamentally different material chemistries. PA 4/6 is a polymeric material, while 50Cr-50Ni-Cb alloy is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 3 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is PA 4/6 and the bottom bar is 50Cr-50Ni-Cb alloy.
Metric UnitsUS Customary Units
Material Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.0 to 16 | |
| 210 |
| Elongation at Break, % | 2.5 to 50 | |
| 5.6 |
| Tensile Strength: Ultimate (UTS), MPa | 120 to 250 | |
| 620 |