PA 4/6 vs. C70620 Copper-nickel
PA 4/6 and C70620 copper-nickel belong to fundamentally different material chemistries. PA 4/6 is a polymeric material, while C70620 copper-nickel is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 3 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is PA 4/6 and the bottom bar is C70620 copper-nickel.
Metric UnitsUS Customary Units
Material Properties
Elastic (Young's, Tensile) Modulus, GPa | 1.0 to 16 | |
120 |
Melting Onset (Solidus), °C | 300 | |
1060 |
Tensile Strength: Ultimate (UTS), MPa | 120 to 250 | |
300 to 570 |