PEEK vs. 356.0 Aluminum
PEEK and 356.0 aluminum belong to fundamentally different material chemistries. PEEK is a polymeric material, while 356.0 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 16 material properties with values for both materials. Properties with values for just one material (30, in this case) are not shown.
For each property being compared, the top bar is PEEK and the bottom bar is 356.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 24 | |
| 70 |
| Elongation at Break, % | 1.6 to 43 | |
| 2.0 to 3.8 |
| Shear Strength, MPa | 50 to 100 | |
| 140 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 97 to 200 | |
| 160 to 240 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 330 | |
| 170 |
| Melting Onset (Solidus), °C | 340 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 1390 to 1700 | |
| 900 |
| Thermal Conductivity, W/m-K | 0.25 to 0.93 | |
| 150 to 170 |
| Thermal Expansion, µm/m-K | 15 to 52 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 to 10 | |
| 15 |
| Stiffness to Weight: Bending, points | 36 to 73 | |
| 53 |
| Strength to Weight: Axial, points | 20 to 41 | |
| 17 to 26 |
| Strength to Weight: Bending, points | 36 to 55 | |
| 25 to 33 |
| Thermal Diffusivity, mm2/s | 0.1 to 0.51 | |
| 64 to 71 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 7.6 to 11 |