PEEK vs. Machinable Glass-ceramic
PEEK and machinable glass-ceramic belong to fundamentally different material chemistries. PEEK is a polymeric material, while machinable glass-ceramic is ceramic. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 16 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is PEEK and the bottom bar is machinable glass-ceramic.
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 120 to 300 | |
| 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 24 | |
| 67 |
| Flexural Strength, MPa | 150 to 330 | |
| 96 |
| Tensile Strength: Ultimate (UTS), MPa | 97 to 200 | |
| 84 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 330 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 1390 to 1700 | |
| 790 |
| Thermal Conductivity, W/m-K | 0.25 to 0.93 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 15 to 52 | |
| 21 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 3.0 to 14 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 to 10 | |
| 14 |
| Stiffness to Weight: Bending, points | 36 to 73 | |
| 51 |
| Strength to Weight: Axial, points | 20 to 41 | |
| 8.8 |
| Strength to Weight: Bending, points | 36 to 55 | |
| 16 |
| Thermal Diffusivity, mm2/s | 0.1 to 0.51 | |
| 0.56 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 4.3 |