PEEK vs. C71520 Copper-nickel
PEEK and C71520 copper-nickel belong to fundamentally different material chemistries. PEEK is a polymeric material, while C71520 copper-nickel is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 16 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is PEEK and the bottom bar is C71520 copper-nickel.
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 24 | |
| 140 |
| Elongation at Break, % | 1.6 to 43 | |
| 10 to 45 |
| Shear Strength, MPa | 50 to 100 | |
| 250 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 97 to 200 | |
| 370 to 570 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 330 | |
| 260 |
| Melting Onset (Solidus), °C | 340 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 1390 to 1700 | |
| 400 |
| Thermal Conductivity, W/m-K | 0.25 to 0.93 | |
| 32 |
| Thermal Expansion, µm/m-K | 15 to 52 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 8.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 to 10 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 36 to 73 | |
| 19 |
| Strength to Weight: Axial, points | 20 to 41 | |
| 12 to 18 |
| Strength to Weight: Bending, points | 36 to 55 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 0.1 to 0.51 | |
| 8.9 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 12 to 19 |