PES vs. B443.0 Aluminum
PES and B443.0 aluminum belong to fundamentally different material chemistries. PES is a polymeric material, while B443.0 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 14 material properties with values for both materials. Properties with values for just one material (35, in this case) are not shown.
For each property being compared, the top bar is PES and the bottom bar is B443.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.6 | |
| 70 |
| Elongation at Break, % | 65 | |
| 4.9 |
| Tensile Strength: Ultimate (UTS), MPa | 87 | |
| 150 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Specific Heat Capacity, J/kg-K | 1100 | |
| 900 |
| Thermal Conductivity, W/m-K | 0.18 | |
| 150 |
| Thermal Expansion, µm/m-K | 53 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.1 | |
| 15 |
| Stiffness to Weight: Bending, points | 33 | |
| 52 |
| Strength to Weight: Axial, points | 18 | |
| 15 |
| Strength to Weight: Bending, points | 32 | |
| 23 |
| Thermal Diffusivity, mm2/s | 0.12 | |
| 61 |
| Thermal Shock Resistance, points | 45 | |
| 6.8 |