PPSU vs. PBI
PPSU belongs to the thermoplastics classification, while PBI belongs to the thermoset plastics. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is PPSU and the bottom bar is PBI.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 140 | |
| 350 |
| Elastic (Young's, Tensile) Modulus, GPa | 3.6 | |
| 5.9 |
| Elongation at Break, % | 26 | |
| 3.0 |
| Flexural Modulus, GPa | 4.7 | |
| 6.5 |
| Flexural Strength, MPa | 130 | |
| 220 |
| Impact Strength: Notched Izod, J/m | 80 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 95 | |
| 160 |
Thermal Properties
| Glass Transition Temperature, °C | 220 | |
| 410 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 210 | |
| 430 |
| Maximum Temperature: Decomposition, °C | 560 | |
| 590 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 340 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 930 |
| Thermal Conductivity, W/m-K | 0.24 | |
| 0.41 |
| Thermal Expansion, µm/m-K | 45 | |
| 23 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.8 | |
| 3.4 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.4 | |
| 3.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 23 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 1.3 |
| Limiting Oxygen Index (LOI), % | 38 | |
| 58 |
| Water Absorption After 24 Hours, % | 0.44 | |
| 0.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.4 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 36 | |
| 46 |
| Strength to Weight: Axial, points | 19 | |
| 34 |
| Strength to Weight: Bending, points | 33 | |
| 50 |
| Thermal Diffusivity, mm2/s | 0.17 | |
| 0.34 |
| Thermal Shock Resistance, points | 42 | |
| 84 |