SAE-AISI 1090 Steel vs. EN 1.0225 Steel

Both SAE-AISI 1090 steel and EN 1.0225 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1090 steel and the bottom bar is EN 1.0225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 280
130 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11
6.7 to 24
Fatigue Strength, MPa 320 to 380
170 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 470 to 570
280 to 290
Tensile Strength: Ultimate (UTS), MPa 790 to 950
440 to 500
Tensile Strength: Yield (Proof), MPa 520 to 610
230 to 380

Thermal Properties

Latent Heat of Fusion, J/g 240
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 46
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82 to 91
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 730 to 1000
140 to 390
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 28 to 34
16 to 18
Strength to Weight: Bending, points 24 to 27
16 to 18
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 25 to 31
14 to 16

Alloy Composition

Carbon (C), % 0.85 to 1.0
0 to 0.21
Iron (Fe), % 98 to 98.6
98 to 100
Manganese (Mn), % 0.6 to 0.9
0 to 1.4
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 0.35
Sulfur (S), % 0 to 0.050
0 to 0.045

Comparable Variants