SAE-AISI 4130 Steel vs. ASTM A572 Steel

Both SAE-AISI 4130 steel and ASTM A572 steel are iron alloys.

For each property being compared, the top bar is SAE-AISI 4130 steel and the bottom bar is ASTM A572 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 300
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13 to 26
18 to 25
Fatigue Strength, MPa 320 to 660
240 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 340 to 640
300 to 380
Tensile Strength: Ultimate (UTS), MPa 530 to 1040
470 to 620
Tensile Strength: Yield (Proof), MPa 440 to 980
330 to 510

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2 to 8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.6
Embodied Energy, MJ/kg 20
22
Embodied Water, L/kg 50
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 180
100 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 2550
290 to 690
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 37
17 to 22
Strength to Weight: Bending, points 19 to 29
17 to 21
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 16 to 31
14 to 18