SAE-AISI 4150 Steel vs. Ferrite
SAE-AISI 4150 steel and ferrite belong to fundamentally different material chemistries. SAE-AISI 4150 steel is a metal, while ferrite is a ceramic material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 12 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 4150 steel and the bottom bar is ferrite.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 to 140 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1310 | |
| 48 to 71 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 470 | |
| 710 to 1050 |
| Thermal Conductivity, W/m-K | 42 | |
| 3.9 to 6.3 |
| Thermal Expansion, µm/m-K | 13 | |
| 8.0 to 9.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.7 to 4.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 15 to 16 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 to 36 |
| Strength to Weight: Axial, points | 24 to 47 | |
| 2.8 to 4.1 |
| Strength to Weight: Bending, points | 22 to 34 | |
| 6.2 to 8.0 |
| Thermal Diffusivity, mm2/s | 11 | |
| 0.78 to 1.9 |
| Thermal Shock Resistance, points | 19 to 39 | |
| 3.0 to 4.6 |