Soda-lime Glass vs. 6065 Aluminum
Soda-lime glass and 6065 aluminum belong to fundamentally different material chemistries. Soda-lime glass is a ceramic material, while 6065 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is soda-lime glass and the bottom bar is 6065 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 to 71 | |
| 68 |
| Poisson's Ratio | 0.23 | |
| 0.33 |
| Shear Modulus, GPa | 29 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 41 to 180 | |
| 310 to 400 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 300 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 720 to 800 | |
| 890 |
| Thermal Conductivity, W/m-K | 1.0 to 1.1 | |
| 170 |
| Thermal Expansion, µm/m-K | 8.8 to 9.0 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.4 | |
| 2.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 16 | |
| 14 |
| Stiffness to Weight: Bending, points | 56 | |
| 49 |
| Strength to Weight: Axial, points | 4.6 to 20 | |
| 31 to 40 |
| Strength to Weight: Bending, points | 11 to 28 | |
| 36 to 43 |
| Thermal Diffusivity, mm2/s | 0.51 to 0.6 | |
| 67 |
| Thermal Shock Resistance, points | 4.7 to 20 | |
| 14 to 18 |