Soda-lime Glass vs. PGA
Soda-lime glass and PGA belong to fundamentally different material chemistries. Soda-lime glass is a ceramic material, while PGA is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 7 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is soda-lime glass and the bottom bar is PGA.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.4 | |
| 1.5 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 to 71 | |
| 6.5 |
| Stiffness to Weight: Axial, points | 16 | |
| 2.4 |
| Stiffness to Weight: Bending, points | 56 | |
| 41 |
| Strength to Weight: Axial, points | 4.6 to 20 | |
| 10 |
| Strength to Weight: Bending, points | 11 to 28 | |
| 21 |
| Tensile Strength: Ultimate (UTS), MPa | 41 to 180 | |
| 55 |