C47940 Brass vs. C28000 Muntz Metal
Both C47940 brass and C28000 Muntz Metal are copper alloys. They have a moderately high 93% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C47940 brass and the bottom bar is C28000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 14 to 34 | |
| 10 to 45 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Shear Strength, MPa | 250 to 310 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 520 | |
| 330 to 610 |
| Tensile Strength: Yield (Proof), MPa | 160 to 390 | |
| 150 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 120 |
| Melting Completion (Liquidus), °C | 850 | |
| 900 |
| Melting Onset (Solidus), °C | 800 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 20 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 23 |
| Density, g/cm3 | 8.2 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 47 | |
| 46 |
| Embodied Water, L/kg | 330 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 100 | |
| 27 to 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 740 | |
| 110 to 670 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 13 to 20 |
| Thermal Diffusivity, mm2/s | 36 | |
| 40 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 11 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 63 to 66 | |
| 59 to 63 |
| Iron (Fe), % | 0.1 to 1.0 | |
| 0 to 0.070 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0.1 to 0.5 | |
| 0 |
| Tin (Sn), % | 1.2 to 2.0 | |
| 0 |
| Zinc (Zn), % | 28.1 to 34.6 | |
| 36.3 to 41 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.3 |